TYVcure UVM
Metakrylathartser
TYVcure UVM has been developed for UV-cured pipe rehabilitation processes. The resin suits for relining and short-liner repair at the same time. The resin can be used as a matrix material for in-situ or for pre-impregnated composites.
TYVcure UVM resin is a methacrylate-based, one-component system that already contains the necessary UV initiator. The resin is completely Styrene-free. The viscosity of the resin can be modified with a thixotropic agent, the amount of which should be adjusted according to the specific application.
| Namn | Värde | Enhet |
|---|---|---|
| Density | 1.1 ± 0.1 | g/cm3 |
| Viscosity (20 min-1) | 3000 ± 400 | mPas |
| Flash point (closed space) | >100 | °C |
| Appearance, color | transparent, yellowish liquid | |
| Namn | Värde | Enhet |
|---|---|---|
| Young’s modulus | > 3000 | MPa |
| Tensile strength | > 25 | MPa |
| Elongation at break | > 0.5 | % |
| Flexural modulus | > 2500 | MPa |
| Flexural strength | > 70 | MPa |
| Compressive strength | > 150 | MPa |
| Shore-D hardness | > 80 | Shore-D |
| Glass-transition temperature | 95 ± 10 | °C |
| Overall chemical resistance | good | - |
För att bedöma kemikalieresistens introducerade vi ett betygssystem från 1 till 5, där 5 indikerar högsta resistens.
| Kemikalie | Resultat |
|---|---|
| Normal petrol | 1 |
| Super petrol | 5 |
| CaCl2– saturated | 5 |
| Diesel | 5 |
| Acetic acid 10% | 3 |
| Acetic acid 20% | 1 |
| Ethanol | 1 |
| Oil | 4 |
| Phosphoric acid 10% | 1 |
| H2O2 30% | 1 |
| H2O2 5% | 2 |
| H2SO4 10% | 5 |
| H2SO4 20% | 2 |
| H2SO4 40% | 5 |
| HCl 10% | 1 |
| HCl 37% | 5 |
| HNO3 10% | 4 |
| HNO3 20% | 1 |
| HNO3 40% | 1 |
| IPA | 1 |
| MgCl2– saturated | 5 |
| NaCl 20% | 5 |
| NaOH 10% | 3 |
| NaOH 30% | 5 |
| NaOH 50% | 5 |
| Lactic acid 10% | 3 |
| Toluol | 2 |